WONDERLITE® PC-110 PC

Hot Search: PP PE ABS

CHEMBULL Markets Featured Suppliers Industry Information

FAILED

WONDERLITE® PC-110 PC | CHI MEI

Price: Negotiable

Appearance: Natural

Stock: 100,000 KG

Negotiable

Product Features

Product Type	Raw Material	Product Categories	PC	CAS NO.	67-07-2
Manufacturers	CHI MEI	Grade	PC-110	Place of Origin	Taiwan - China
Appearance	Natural	Packing Size	25/KG Standard Packaging
Usage level	Commercial Grade			Feature level	Transparency Grade, High Impact Resistance
Processing Method	Injection Molding			Shape	Particle

Physical Parameters

Test Item

Test Method

Test Condition

Test Unit

Test Result

Typical properties

Melt Flow Index	ISO 1133	300℃, 1.2kg	ml/10 min	10
Spiral flow	CHIMEI	260℃,2mm,V:50%,P:50%	cm	-
Mass Density	ISO 1183	23℃	g/cm³	1.2
Tensile Strength at Yield	ISO 527	50mm/min	MPa	65
Tensile Strength at Break	ISO 527	50mm/min	MPa	75
Tensile Elongation	527	50mm/min	%	120
Flexural Strength	178	2mm/min	MPa	90
Flexural Modulus	178	2mm/min	GPa	2.4
Izod Impact Strength	ISO 180/4A	23℃,1/8” Notched	kJ/m²	75
Izod Impact Strength	ISO 180/4A	-30℃,1/8” Notched	kJ/m²	-
Charpy Impact Strength	ISO 179	23℃,1/8” Notched	kJ/m²	75
Charpy Impact Strength	ISO 179	-30℃,1/8” Notched	kJ/m²	-
Vicat Softening Temperature	ISO 306	1Kg,50 ℃/hr	℃	150
Vicat Softening Temperature	ISO 306	5Kg,50 ℃/hr	℃	145
Heat Distortion Temperature	ISO 75/A	1.8 MPa Unannealed	℃	128
Heat Distortion Temperature	ISO 75/A	1.8 MPa Annealed	℃	143
Dielectric Constant	IEC 60250	1MHz	-	-
Volume Resistivity	IEC 60093	-	Ohm X m	-
Surface Resistivity	IEC 60093	-	Ohm	-
Coefficient of Linear Thermal Expansion	ISO 11359	-	-	6.0~8.0x10-5
Flammability	UL 94	-	-	2.5mm V-2
Mold Shrinkage	ISO 294-4	-	%	0.5~0.7