INFINO LT-1100 PC | Lotte Chem
Price: $2.74/KG
Appearance: Transparent
Stock: 25,000 KG
KG
Total Amount
$68.5
Details
Product Features
| Product Type | Raw Material | Product Categories | PC | CAS NO. | 67-07-2 |
|---|---|---|---|---|---|
| Manufacturers | Lotte Chem | Grade | LT-1100 | Place of Origin | Korea |
| Appearance | Transparent | Packing Size | 25/KG Standard Packaging | ||
Physical Parameters
Test Item
Test Method
Test Condition
Test Unit
Test Result
Thermal properties
Heat distortion temperature | ASTM D648 | 18.56kgf/cm2, 6.4mm | ℃ | 128 |
Vicat softening temperature | ISO 306 | B/50 | ℃ | 143 |
Electrical properties
Specific Gravity/Density | ASTM D792 | Natural或代表color | - | 1.19 |
Melt index | ASTM D1238 | 300℃, 1.2kg | g/10min | 10.5 |
Melt index | ASTM D1238 | 250℃, 10kg | g/10min | 25.4 |
Mold shrinkage (MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.5-0.7 |
Mold shrinkage (TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.5-0.7 |
Mechanical Properties
Tensile strength (at yield) | ASTM D638 | 50mm/min | kgf/cm² | 640 |
Elongation at break | ASTM D638 | 50mm/min | % | 110 |
Tensile modulus | ASTM D638 | 50mm/min | kgf/cm² | 22500 |
Breaking strength (at break) | ASTM D638 | 50mm/min | kgf/cm² | 660 |
Bending strength | ASTM D790 | 2mm/min | kgf/cm² | 920 |
Flexural modulus | ASTM D790 | 2mm/min | kgf/cm² | 23000 |
lzod impact strength (notched) | ASTM D256 | 1/4 inch at 23℃C | kgf-cm/cm | 10 |
lzod impact strength (notched) | ASTM D256 | 1/8 inch at 23℃C | kgf-cm/cm | 87 |
Hardness | ASTM D785 | R-Scale | - | 122 |
Recommended
FT5230 LDPE | Borouge
Negotiable
POLYLAC® PA-717CK ABS | CHI MEI
Negotiable
EPR27LS PA66 | SHENMA
Negotiable
InnoPlus LD2426H LDPE | PTTGC
Negotiable
M90 POM | Xinjiang Guoye
Negotiable